| PART A | ||
| PARTICULARS OF SAMPLE SUBMITTED | ||
| a) Name of Sample (as stated by party) | : | Wood Polymer Composite Foamed Board |
| b) Grade / variety / type / size / class | : | NA |
| c) Declared value, if any | : | NA |
| d) Code No. | : | NA |
| e) Batch No. and Date of Manufacture | : | NA |
| f) Quantity | : | 02 Nos |
| g) Mode of Packing | : | Packed in bag |
| h) Date of Receipt | : | 11.09.2015 |
| i) Date of completion | : | 17.11.2015 |
| j) Sealed or not | : | NA |
| k) Any other information | : | NA |
| PART B | ||
| SUPPLEMENTARY INFORMATION | ||
| a) Reference to sampling procedure | : | Samples Supplied by the Party |
| b) Supporting documents for the measurement taken and result derived | : | As per Part C |
| c) Deviation from the test method as prescribed in relevant work Instructions | : | As per Standard |
| Wood Polymer Composite Foamed Board | Test Report No. 3336 | |||
| Dated : 17.11.2015 | ||||
| PART C TEST RESULTS |
||||
| Sr. No. | Tests | Test Method | Unit | Results Obtained |
| 1 | Density | IS 2380 (P-3) | Kg/m3 | 624.6 |
| 2 | Moisture Content | IS 2380 (P-3) | % | 0.85 |
| 3 | Water Absorption 1) 2 Hour Soaking 2) 24 Hours Soaking |
IS 2380 (P-16) | % | 2.85 4.76 |
| 4 | Swelling in Water 1) Length 2) Width 3) Thickness |
IS 2380 (P-17) | % | 0.25 0.32 1.5 |
| 5 | Thickness Swelling due to Surface Absorption |
IS 2380 (P-17) | % | 7.5 |
| 6 | Modulus of Rupture 1) Average 2) Minimum |
IS 2380 (P-4) | N/mm2 | 18.2 16.8 |
| 7 | Tensile Strength (Perpendicular to Surface) |
IS 2380 (P-5) | N/mm2 | 0.47 |
| 8 | Tensile Strength (Perpendicular to Surface) After cycle Test |
IS 2380 (P-5) | N/mm2 | 0.23 |
| 9 | Tensile Strength Accelerated Water Resistance Test |
IS 2380 (P-5) | N/mm2 | 0.17 |
| 10 | Screw Withdrawal Strength 1) Face 2) Edge |
IS 2380 (P-14) | N | 1330 916 |
| PART D | ||
| REMARKS | : | NIL |
| NOTE | 1 | The results related only to the items tested |
| 2 | The report shall not be reproduced in full/part without written approval of the laboratory | |